Carbon monoxide catalyst/ Hopcalite / CuO and MnO2 mixture
Precious metal catalysts for CO, which belongs to the Palladium catalysts, palladium content at 2%. The catalyst for catalytic CO gas at normal temperature and pressure, the CO and O2 in the air generates CO2. Its biggest advantage is that performance, in the context of larger water vapor (RH>85%) can still be stable catalyst and catalytic effect of low concentrations of CO gas has good. Compared to conventional hydrophobic CO catalysts, precious metal catalysts have significant performance advantages and advantagesWorking principlethe catalyst density is 0.5G/ml, the granular structure, diameter of 2~4mm, with good breathability. When in use, forcing air through the catalyst layer you want. In a closed environment, ensure CRE 4~6 times, CO concentration can be controlled in the following 24ppm. According to experience, in 8m3 in the space below, 4kg CO catalysts effective in 8~12 space, 5kg CO catalysts within the space of 12~16 M3, 6kg CO catalysts. In spaces greater than 16 M3, increased according to catalyst quantity and number of air purifiers.
Technical parameters |
Absorption depth |
≤0.5ppm |
Bulk density |
50g/ml |
Particle size |
φ1.5×1~5mm |
Crushing strength |
>70N |
Adsorption capacity |
≥50ml/g |
Adsorption operation conditions |
Bed temperature |
18-50Degrees Celsius |
Air speed ratio |
≤5000 h-1 |
Operating pressure |
0.4~2.5Mpa |
|
|
Ratio of height to diameter |
≥8 |